Yellow 10P150
CI Pigment Yellow 227
Niobium Sulfur Tin Zinc Oxide

A chromatic yellow inorganic pigment produced by high temperature calcination. This pigment has excellent UV and visible opacity, is chemically inert, heat resistant, and stable to ultraviolet light. It is non-bleeding and non-migratory. It has exceptional durability and hiding power, and is generally used in applications where resistance to heat, light, and weather are needed. It is compatible with most resin systems and polymers, and is non-warping. Typical applications (non inclusive) are plastics and other applications where equivalent pigment chemistry is used. This material is patented under US Patent 8,192,541, and foreign patents have been applied for under WO/2011/156362, PCT/US2011/039432.

Specifications:


Specific Gravity

5.5

Oil Absorption

11 kg/100 kg

Residue 325 mesh [44 µm]

0.01 wt%

pH

5.4

Heat Stability

320 °C

Surface Area BET

3.5 m²/g

Conductivity

14 µS/cm

Percent Moisture

0.1 wt%

Crystal Structure

Pyrochlore

Lightfastness

8 (1-8)

Weatherability

5 (1-5)

Acid Resistance

5 (1-5)

Alkali Resistance

5 (1-5)

Bulk Density

0.80 kg/L

Mean Particle Size

0.9 µm

HBU

21 °C

TSR

73 %

UV Opacity @ 340nm

0.0 %

Reflectance (300-2500nm)

Reflectance (visible only)